200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY625
payment methodT/T, L/C, Westem Union
update timeTue, 05 Nov 2013 12:12:53 GMT
color white
HS code 39100000
sample available
normal packing 25kgs per drum
delivery within 3 days
usage for mold making
MOQ 200kgs
type liquid
application gypsum, resin
Min Order200 kilogram
tin catalyst silicone rubber applications
tin catalyst silicone rubber is primarily intended for poly resin crafts, PU crafts, PU resin crafts ,gypsum crafts ,unsaturated resin crafts, lighting and candles crafts ,plastic toy , stationery gifts crafts industry, a large statue Buddha, furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, largescale cement mold, artificial fossils Factory, Europe component factory,
simulation landscapes, animals and plants sculpture, sandstone crafts and so on.
tin catalyst silicone rubber description
tin catalyst silicone rubber is white or red flowing liquid with general hardness of 22-50 shore A after curing. tin cured silicone rubber is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation.
FAQ. Why the gypsum mold making silicone just can be reproduced for a few times?
It can be due to the following reasons:
a. Adding too much silicone oil in to silicon rubber. Silicon oil is an additive which destroies the molecular weight of silicone rubber and reduce the tension and tear strength.
b. Using the silicon rubber with a high hardness to make molds for small sized products with delicate and intricate designs and the silicon rubber with a low hardness to makes molds for large sized products with simple designs.
(Notes: we should choose the silicon rubber specifically according to the requirements of our products to avoid this problem.)
Datesheet of gypsum mold making silicone.
Property | 625# | 630# |
Hardness (Shore A) | 25 | 30 |
Tensile strength, MPa | 3.1 | 3.6 |
Elongation @ break, % | 580 | 550 |
Tear Strength (N/mm) | 25 | 32.6 |
Linear shrinkage (%) | 0.3 | 0.3 |
Viscosity | 19000-22000 | 23000-25000 |
Color | Off White | Off White |
Mixing ration | 100:5 | 100:5 |
Pot life | 40 minutes | 30 minutes |
Cure time | 4-5 hours | 4-5 hours |
gypsum mold making silicone Manufacturing instruction:
Add curing agent of 2%-3% at the room temperature, the gypsum mold making silicone is still operational within 30 minutes, and in 2-3 hours.
1. Adding curing agent 1%, the gypsum mold making silicone can still be operated within 2. 5 hours and can be demoulded after 6-8 hours.
2. Adding curing agent 2%, the gypsum mold making silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
3. Adding curing agent 3%, the gypsum mold making silicone can still be operated within 30 minutes and can be demoulded after 1. 5-2 hours.
4. Adding curing agent 4%, the gypsum mold making silicone can still be operated within 15 minutes and can be demoulded after 1-1. 5 hours.
Any questions of gypsum mold making silicone , please feel free to contact Cassi :
TEL: 086-755-89948006
FAX: 086-755-89948030
MOBILE:086-15220073603
Website: www(dot)szrl(dot)net
E-MAIL: hyjg(at)szrl(dot)net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.