GRADE 310S STAINLESS STEEL WIRE

310S is an AOD melted austenitic stainless steel with high chromium and nickel content.  This alloy has excellent resistance to oxidation at high temperatures making it suitable for furnace rails and dunnage.  This grade is used often in carburizing atmospheres that are common in petrochemical industries.

 

SPECS USAP PRODUCES TO:

l AMS 5651

l AMS-QQ-S-763

l ASTM A276

l ASTM A479

 

INDUSTRY / TRADE NAMES

l UNS S31008

l UNS S31009

l 1.4845

 

APPLICATIONS:

The higher alloyed stainless steels generally have excellent strength at elevated temperatures along with outstanding resistance to creep deformation and environmental attack. Therefore, stainless 310s is used widely in industries such as heat treatment and chemical processing. Some examples include:

l Furnace Parts

l Oil Burner Parts

l Welding Filler Wire and Electrodes

l Annealing Covers

l Fire Box Sheets

 

Chemical Properties:

%	Cr	Ni	C	Si	Mn	P	S	Mo	Cu	Fe
310S	min: 24.0 max:26.0	min: 19.0 max: 22.0	0.08	1.00	2.0	0.045	0.030	0.75	0.5	balance

 

Mechanical Properties:

Grade	Tensile Strength ksi (min.)	Yield Strength 0.2% Offset ksi (min.)	Elongation - % in 50 mm (min.)	Hardness (Brinell) MAX	Hardness (Rockwell B) MAX
310S	75	30	40	217	95

 

FORMS

l Continuous Coils

l Cut to lengths

l Precision cutting

 

Stainless Steel 310S Wire Specification :

l Standard : 310S / 1.4845

l Range : 0.10mm to 8.00mm Required Size

l Designation : ASTM A164, ASME SA164

l Type : Wire Bobbin, Wire Coil, Filler Wire, Coils, Wiremesh

l Finish: Soft annealed - ¼ hard, ½ hard, ¾ hard, full hard (Matte or Bright finish)

 

STANDARD WIRE FINISHES

l Extra Clean: (XC) Extra clean is also referred to as “bright annealed” or “bright annealed and cold rolled”

l Grease (round wire only): Drawn in a heavy grease produces an “Ultra bright” finish for

l decorative applications Soap (round wire only):

l Soap is used as a lubricant in the drawing process and is not removed. It acts as a lubricant during customer part forming operation. A soap finish is available in tempered products.

l Plated: Many plating options are available. ∗Special finishes are available: Contact Ulbrich Wire Sales with special finish and plating requests.

 

CORROSION RESISTANCE:

l Provides excellent corrosion resistance

l High chromium content allows for good aqueous corrosion resistance

l Excellent resistance at normal temperatures and also has good resistance to oxidizing and carburizing atmospheres

 

HEAT RESISTANCE:

l Good resistance to oxidation in intermittent service in air at temperatures up to 1040°C and 1150°C in continuous service.

l Good resistance to thermal fatigue and cyclic heating.

l Widely used where sulphur dioxide gas is encountered at elevated temperatures.

l Continuous use in 425-860°C range not recommended due to carbide precipitation, if subsequent aqueous corrosion resistance is needed

l Generally used at temperatures starting from about 800 or 900°C – above the temperatures at which 304H and 321 are effective.

 

FABRICATION:

l Commonly used in the heat treatment and process industries due to high temperature and corrosive environments

l Often fabricated into complex structures

l Roller-forms, stamps and draws readily

l Because 310s work hardens, severe forming operations should be followed by an anneal

 

WELDABILITY:

l Austenitic stainless steel is generally considered to be weldable

l Generally considered to have weldability equivalent to 304 and 304L

l Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion