1.2562 142W12 Cold Work Tool Steel
group nameTool Steel Bars
-
Min Order1 piece
brand namefushun
model1.2562 142W12
payment methodL/C, T/T
-
update timeTue, 25 Apr 2023 11:15:15 GMT
Paramtents
Process hot rolled or hot forged
Delivery Condtion annealed
Surface Condition smooth, bright
Packging & Delivery
Min Order1 piece
Briefing
Detailed
1.2562 142W12 Cold Work Tool Steel
Description
Low alloyed W cold working tool steel.The high quality Germany DIN 1.2562 material is one of the more steel grades we supply, Alloyed WV steel.
Applications
Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring tools.
Chemical Composition (in weight %)
Grade | C | Si | Mn | Cr | V | W |
1.2562 | 1.43 | 0.23 | 0.30 | 0.35 | 0.25 | 3.05 |
Mechanical Properties of 1.2562
Rp0.2 (MPa) | Rm (MPa) | Impact KV (J) | Elongation A (%) | A Z (%) | Delivery | Hardness HB |
715 (≥) | 459 (≥) | 31 | 34 | 23 | Solution & Aging, Ann, Ausaging, Q+T | 314 |
Soft Annealing
Heat to 720-750℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 270.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650℃, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 800-830℃ followed by water quenching. Hardness after quenching is 66 HRC.
Tempering
Tempering temperature: 100-250℃.
Forging
Hot forming temperature: 1050-850℃.
You need a product
You May Like
6YRS FUSHUN Metals
- Nearest port for product export
- Tianjin, Qingdao, Shanghai, Huangshi
- Delivery clauses under the trade mode
- FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
- Acceptable payment methods
- T/T, L/C, D/P D/A