Flurine® Wide molecular weight distribution Fluoroelastomer

  • group nameFluoroelastomer FKM

  • Min Order1 kilogram

  • brand nameZheflon PVDF & Flurine FKM Manufacturer

  • model26404,6504,26704

  • payment methodT/T, L/C

  • update timeTue, 05 Nov 2024 13:43:59 GMT

Paramtents

  • Features Wide molecular weight distribution

  • Uses Shaft seals, gaskets, O-rings, extruded shapes, mo

  • Forms White or light-yellow flake

Packging & Delivery

  • Min Order1 kilogram

Briefing

Used in many industries including automotive, fluid power, appliance and chemical industries.

Detailed

Description
Flurine® 26404,26504 and 26704 are wide molecular weight distribution Fluoroelastomer, which is comprised of vinylidene fluoride (VF2) and hexafluoropropylene (HFP).

Frequently used in many industries including automotive, fluid power, appliance and chemical industries. It improves the processing performance and has good fluidity.

It is resistant to oils, fuels, aliphatic series, aromatic hydrocarbons, lubricants, and most mineral acids.
Technical Specifications
General
FeaturesWide molecular weight distribution
UsesShaft seals, gaskets, O-rings, extruded shapes, molded tubing
FormsWhite or light-yellow flake
ItemsTypical ValueTest Method
264042650426704
Physical Properties
Fluorine Content(mass%)666666
Density(g/cc)1.81~1.831.81~1.831.81~1.83ASTM D297
Mooney Viscosity40~4950~5965~79ASTM D1646 ML 1+10 at 121°C
Water content0.10.080.08ASTM D 5668
SolubilitySoluble in lower ketones and esters
Vulcanization Properties
T10(s)<70<70<70ASTM D5289
T90(s)<140<140<140ASTM D5289
Mechanical Properties
Tensile strength(MPa)141414ASTM D412 Method A
100% Modulus4.855.2ASTM D412 Method A
Elongation at Break(%)170170170ASTM D412 Method A
Tearing Strength(KN/m)191919ASTM D624
Hardness, Shore A747474ASTM D2240, Type A
Compression Set181818ASTM D395, Test B 70 hours at 200℃
Air-oven agingISO 188 After Dry Heat Aging;70 hours at 230℃
Tensile strength change rate(%)-15-12-10ASTM D412 Method A
Elongation at Break change rate(%)-10-8-6ASTM D412 Method A
Hardness change, Shore A-2-2-1ASTM D2240, Type A 
Thermal Properties
Glass Transition Temp, Tg(℃)-20-20-20ASTM D1329
Brittleness Temperature(℃)-30-30-30ASTM D2137
Chemical resistance Properties
Resistance to liquids3 # standard oil
Volume change rate(%)222ASTM D471 72 hours at 150℃
Mass change rate(%)11ASTM D471 72 hours at 150℃
FormulationCuring condition
Polymer            100      MT carbon black,N990   30PressOven
Calcium hydroxide    6        Magnesium oxide         3
Fluorocure-5#        2.56min at 177°C24h at 230°C
Process Safety Instructions
1)Store and use all fluoroelastomers only in a well-ventilated area.
2)Do not smoke in areas contaminated with dust from fluoroelastomers.
3)Avoid eye contact. After handling fluoroelastomers wash any skin that came in contact with the product with soap and water.
4)Potential hazards, including evolution of toxic vapors, exist during compounding or processing under high temperatures. 
5)Before processing the fluoroelastomers, read and consult the MSDS, and follow all label directions and operation cautions..
Packaging And Storage
1)Fluoroelastomers be packed in PVC bags in the shape of rubber film, each bag weight 5KGS, and finally be put into a carton. Each carton contains 5 bags with net weight 25KGS.
2)It must be stored in a clean, cool, and dry place. The storage life is one year from the date of production. It must be re-inspected if over one year and only can use if qualified.
3)It is transported as non-dangerous chemicals. Avoid excessive vibration and far away from pollution, sunshine and water during the transport.
Nearest port for product export
Ningbo, Shanghai
Delivery clauses under the trade mode
FOB, CFR, CIF, EXW, Express Delivery
Acceptable payment methods
T/T, L/C
Contact Suppliers

Follow this Suppliers