PolyAdds Antioxidant Newanox 245 36443-68-2
group nameAntioxidant
-
Min Order1 piece
brand namePolyAdds Chemical Additive Supplier
modelNewanox 245
payment methodL/C, T/T
-
update timeSat, 21 Sep 2024 13:44:53 GMT
Paramtents
CAS 36443-68-2
Appearance White, free-flowing powder
Molecular Weight 586.8 g/mol
Melting Range 76-79°C
Flash Point > 150°C
Packging & Delivery
Min Order1 piece
Briefing
PolyAdds Antioxidant Newanox 245 is a hindered phenolic antioxidant that protects substrates from thermal oxidative degradation during manufacturing, processing, and end use.
Detailed
Physical Property:
Appearance: White, free-flowing powder
Chemical Composition: Ethanediol bis(ethylene) bis(3-(5-tert-butyl-4-hydroxy-m-tolyl) propionate)
Molecular Weight: 586.8 g/mol
Melting Range: 76-79°C
Flash Point: > 150°C
Vapor Pressure at 20°C: 4 E-8 Pa
Density at 20°C: 1.14 g/mL
Solubility at 25°C (g / 100 g solution):
- Acetone: > 50
- Benzene: 18
- Chloroform: > 40
- Ethyl Acetate: 37
- Ethanol: 10
- n-Hexane: < 0.1
- Methanol: 12
- Methylene Chloride: > 40
- Toluene: 6
- Styrene: 6
- Polyether: ~3
- Water: < 0.01
Volatility (TGA, air, heating rate 20 K/min):
- Temperature for 1% weight loss: 280°C
- Temperature for 10% weight loss: 330°C
Application:
PolyAdds Antioxidant Newanox 245 is highly effective in styrene polymers, especially impact-modified polystyrene (HIPS), ABS, MBS, SB, and SBR latexes, as well as in POM homopolymers and copolymers. In addition to imparting thermal stability to the final polymer, it also acts as a chain terminator in PVC polymerization.
FAQs:
description
PolyAdds Antioxidant Newanox 245 is a hindered phenolic antioxidant that protects substrates from thermal oxidative degradation during manufacturing, processing, and end use.
features
High extraction resistance，Low volatility，Odorless，Good color stability
Package
25kg/pack
You need a product
You May Like
6YRS PolyAdds
- Nearest port for product export
- Shanghai
- Delivery clauses under the trade mode
- FOB, CFR, CIF, EXW, FCA, DDP, DDU
- Acceptable payment methods
- T/T, L/C